161 The Corrosion Resistance of Zn-11% Al-3% Mg-0.2% Si Hot-dip Galvanized Steel Sheet Yasuhide MORIMOTO, Masao KUROSAKI, Kazuhiko HONDA, Kazumi NISHI
|
|
- たかとし おいもり
- 2 years ago
- Views:
Transcription
1 161 The Corrosion Resistance of Zn-11% Si Hot-dip Galvanized Steel Sheet Yasuhide MORIMOTO, Masao KUROSAKI, Kazuhiko HONDA, Kazumi NISHIMURA, Satoru TANAKA, Akira TAKAHASHI and Hidetoshi SHINDO Synopsis : For the improvement on corrosion resistance of Zn-5mass%-0.1mass%Mg hot-dip galvanized steel sheet, it was investigated that the influence of Al and Mg contents and Si addition in coating on the corrosion resistance of the coating. It was found that the corrosion resistance of Zn-11mass%A1-3mass%Mg-0.2mass%Si galvanized steel sheet is more than 5 times superior to Zn-5mass%Al-0.1mass%Mg galvanized steel sheet in the corrosion loss the SST, and also superior to that in the outdoor exposure test. According to the polarization measurements in the 5mass% NaCl solution, further additions of Al, Mg and Si in the Zn-5mass % Al- 0.1mass%Mg coating decreased the both anode and cathode currents. This effect is regarded as one of reasons of enhancement of corrosion resistance in the SST. It is supposed that the increased polarization is related to the thickness and stability of basic zinc chloride as the corrosion product formed on the Zn-11%Si coating. Key word : hot-dip galvanized steel sheet; corrosion; Mg; Si. 161
2 162 Fig. 1. Effect of Al addition to the coating on corrosion resistance. (After the 500 h SST) Fig. 2. Effect of Mg addition to the coating oncorrosion resistance. (After the 500 h SST) Fig. 3. Effect of Si addition to the coating oncorrosion resistance. (After the 500 h SST) 162
3 Znー11% B A Fig. 4. The appearance 0.2%Si. of specimens the 500h Al お よ び Mg 含 有 率 を 高 め,さ ア ノ ー ド電 流,カ Si め っ き 鋼 板 の 耐 食 性 B: Zn-11%Mg, C: Zn-11%Mg- Si ら に Si を 添 加 す る こ と で, Fig. 6. Polarization curves of the specimens mersion in 5% NaCl solution for 3 h. ソ ー ド電 流 が と も に 低下 し て い る つ ま り, ア ノ ー ド反 応 で あ る め っ き皮 膜 の 溶 解 反 応, C SST. A: Zn-5%A1-0.1%Mg, Fig. 5. Cross-sectional image of Zn-11% coating. a: SE image, b: Zn c: Mg d: Al. the im- カ ソー ド 反 応 で あ る酸 素 の 還 元 反 応 の 両 者 が 抑 制 され て い る こ とが わ か る. Fig. 7 に, Zn-11% 物 に 覆 わ れ て い る こ と が わ か る Zn-5% 霧 試 験 24 時 間 後 の GDS Si め っ き 鋼 板 の 塩 水 噴 11% 濃 化 が み ら れ る そ の下 層 に は 主 と し て Al が 存 在 す る こ 0.2% Siめ と が わ か る こ の こ と か ら, Si を 含 有 す る 腐 食 生 成 物 が 緻 密 で あ り, 含 有 し た 腐 食 生 成 物 で 覆 わ れ て お り, と Si を そ の下 層 に Alリ っ si め っ き の 腐 食 生 成 物 は 緻 密 な 形 態 を し て い る こ と が わ か る こ の こ と か ら,Zn-11% は Mg, Si お よ び O の め っ き の 最 表 層 は Mg Mgめ き の 腐 食 生 成 物 が 粒 状 で 粗 な 外 観 で あ る の に 対 し, Zn - に よ る 深 さ 方 向 の 分 析 結 果 を 示 す 図 よ り, め っ き の 表 層 か ら 深 さ 1μm Al-0.1% っ き は 腐 食 初 期 に め っ き 表 層 に 生 成 す る,Mg 護 作 用 を 有 す る た め, ッ Zn-5% チ 層 が 存 在 す る も の と 考 え ら れ る. め っ き 皮 膜 の 塩 水 噴 霧 試 験 24 時 間 後 に お け る 表 面 の Al-0.1% Mg Mgと め っ き に 対 す る保 塩 水 噴 霧 環 境 に お け る耐 食 性 が め っ き に比 べ て 向 上 して い る と 考 え ら れ る. 3 3 SEM 観 察 結 果 を Fig. 8 に 示 す い ず れ の め っ き も塩 水 噴 霧 試験 前 の 外 観 は平 坦 で あ るが,試 験 後 の 表 面 は 凹 凸 が 存 在 屋 外 曝 露 試験 に お け る め っ き の腐 食 挙 動 Fig. す る外 観 と な っ て お り,い ず れ の め っ き も全 面 が 腐 食 生 成 0.1% 163 Mg 9 に, 鋼 板, 沖 縄 に て Zn-11% 1.5 年 問 屋 外 曝 露 さ れ た Zn-5% Si Al- め っ き 鋼 板 の 外 163
4 1164 鉄 と鋼 Tetsu-to-Hagane Vol.89 (2003)No. 1 Fig. 7. GDS depth profile of Zn-11%Mg-0 of the specimens C the 24 h SST. a: Zn-5%A1-0.1%Mg, b: Zn-11%Mg, c: Zn-11%Al B A Fig. 9. The appearance of outdoors exposed specimens Okinawa for 1.5 years. A: Zn-5%Al-0.1%Mg, Zn-11%A1-3% Si. 観 に つ い て 示 す 図 よ り, 11%Al-3 the 24 h SST. b a Fig. 8. Surface SE images 3% Si..2%Si % Mg-0.2 at B: 屋 外 曝 露 環 境 に お い て もZnー % Si め っ き 鋼 板 はZn-5 % Al0.1%Mg 鋼 Fig. 10. XRD doors 板 に 比 べ て 白 錆 の 発 生 が 少 な く, 良 好 な 耐 食 性 を 示 す こ と intensity of corrosion products exposed at Okinawa for 1.5 years. out- が わ か る. Fig.10に, 曝 露 試 験 片 の 腐 食 生 成 物 をx線 回 折 に よ っ て 分 析 した 結 果 を示 す Zn-5 % Al-0.1%Mg 徴 で あ る Zn の 溶 解 に よ っ て 生 成 す る腐 食 生 成 物 は 初 期 鋼板 につ い て は は塩 基 性 塩 化 亜鉛 で あ り, 塩 基 性 塩 化 亜 鉛 が 導電 性 を有 す 塩 基 性 塩 化 亜 鉛 お よ び 塩 基 性 炭 酸 亜 鉛 の 他 に酸 化 亜 鉛 が 腐 る 酸 化 亜 鉛 に 変 化 す る こ とで 腐 食 生 成 物 の 保 護 性 が 弱 ま 食 生 成 物 と して 存 在 す る が,Zn-11 る6) この 結 果 か ら, Zn-11%Mg-0.2 % Al-3 % Si に お い て は 腐 食 生 成 物 中 に 酸 化 亜 鉛 が検 出 され な い こ と が特 に お い て は 塩 基 性 塩 化 亜 鉛 がZn-5%Al-0,1 164 % Si め っ き鋼 板 % Mg 鋼 板 に比
5 165 1 ) U.S.Patent No , (1977). 2 ) K.Tano and S.Higuchi: Seitetsu Kenkyu, 315 (1984), ) J.Pelerin, B.Bramaud, D.Coutsouradis and S.Radtke: J. Met. Finish. Soc. Jpn., 33 (1982), ) A.Komatsu, H.Izutani, T.Tsujimura, A.Andou and T.Kittaka: Tetsuto-Hagane, 86 (2000), ) D.J.Blrickwede: Tetsu-to-Hagane, 66 (1980), ) Y.Miyoshi, J.Oka and S.Maeda: Trans. Iron Steel Inst. Jpn., 23 (1983),
Factors Controlling the Paint Adhesion of Zinc Alloy Electroplated Steel Sheets Kazumi NISHIMURA, Minoru KITAYAMA and Yasuhiko MIYOSHI Synopsis : Corr
Factors Controlling the Paint Adhesion of Zinc Alloy Electroplated Steel Sheets Kazumi NISHIMURA, Minoru KITAYAMA and Yasuhiko MIYOSHI Synopsis : Corrosion resistance of Zn alloy electroplated steel sheets
More information893 Table 1. CCT condition. Fig.1.Shematic figure for measuring corrosion potential. Salt spray test of 2 weeks Fig.2.Relation between blister width a
892 Effect of Test Conditions on the Corrosion of Painted Zn-Alloy- Electroplated Steel Sheets Kazumi NISHIMURA, Yasuhiko MIYOSHI and Takashi HADA Synopsis : Cyclic Corrosion Test (CCT) and Salt Spray
More informationUDC : ' : '24' : '24'26' : : A Study of Condition of Pits Formation and Their Fe
UDC 620.193: 669.15'26-194.3: 669.15'24'26-194.3: 669.15'24'26'28-194.3: 669.141.24: 621.385.833.2 A Study of Condition of Pits Formation and Their Features in Chloride Solution Norio FUKASAKO, Hirokazu
More informationステンレス鋼用高性能冷間鍛造油の開発
Development of High Performance Cold Forging Oil for Stainless Steel Toshihide Ohmori, Kazuhiko Kitamura ClP ( ) Cl P-Zn ( P ) ClP-Zn High performance cold forging oil for stainless steel has been developed
More information3. 暴 露 試 験 3-1 暴 露 試 験 方 法 大 気 暴 露 試 験 は JIS Z 2381 大 気 暴 露 試 験 方 法 通 則 に 準 じた 直 接 暴 露 試 験 方 法 暴 露 試 験 片 は 45 度 の 角 度 で 架 台 に 取 り 付 けた ( 写 真 4~5 参 照 )
溶 融 亜 鉛 めっきの 耐 食 性 に 対 する 火 山 ガスの 影 響 一 般 社 団 法 人 日 本 溶 融 亜 鉛 鍍 金 協 会 技 術 標 準 化 委 員 会 耐 食 性 グループ 1.はじめに 鋼 材 の 腐 食 に 大 きく 影 響 を 与 える 要 因 として 海 塩 粒 子 とともに 硫 化 水 素 ガ ス 亜 硫 酸 ガスが 挙 げられる 日 本 は 火 山 国 であり 全 国
More informationCuおよびCu‐Sn系化合物のSn‐Pbはんだ濡れ性解析
61 Wettability of Cu and Cu-Sn Intermetallic Compound by Sn-Pb Solder Alloy Hisaaki Takao, Nobuyuki Yamamoto, Hideo Hasegawa CuCu-Sn Cu 150 C 2h55nmCu 2 O Cu Cu-Sn 5nm Cu-Sn Cu SnCu-Sn Wettability of Cu
More informationEffect of WC Grain Size on Corrosion Resistance of WC-Co Cemented Carbide Shuichi Imasato, Shigeya Sakaguchi, Taikou Okada and Yasunori Hayashi *1 Nip
Effect of WC Grain Size on Corrosion Resistance of WC-Co Cemented Carbide Shuichi Imasato, Shigeya Sakaguchi, Taikou Okada and Yasunori Hayashi *1 Nippon Tungsten Co., Ltd., 3173-2 Oaza-sonobe Kiyama-cho
More informationCorrosion Wear of Alloy Tool Steel (SKD 11) Coated with VC and Precipitation Hardening Stainless Steel (SUS 630) in Sodium Chloride Aqueous Solution T
Corrosion Wear of Alloy Tool Steel (SKD 11) Coated with VC and Precipitation Hardening Stainless Steel (SUS 630) in Sodium Chloride Aqueous Solution Toshiyuki TANAKI*, Makoto YUASA** and Isao SEKINE***
More informationAl-Si系粉末合金の超塑性
Superplasticity of Al-Si P/M Alloys Satoru Ishihara, Mikio Kondoh, Kazuhiko Itoh Al-17Si-4.5Cu-0.5Mg-(06)Fe-(02)Mm ( Mm : ) (i) (ii) Si(iii) Fe (iv) Mm Al-17Si-4.5Cu-0.5Mg500 10 2 s 1 520 110 1 s 1 Si
More informationT05_Nd-Fe-B磁石.indd
Influence of Intergranular Grain Boundary Phases on Coercivity in Nd-Fe-B-based Magnets Takeshi Nishiuchi Teruo Kohashi Isao Kitagawa Akira Sugawara Hiroyuki Yamamoto To determine how to increase the coercivity
More informationTable 1. Bath composition and plating conditions. Fig. 1. Relationship between surface roughness of zinc electrodeposits from sulfate bath and coating
Effects of Electrolysis and Bath Conditions on the Surface Roughness, Morphology and Crystal Orientation of Zinc Electrodeposit Masaru SAGIYAMA, Masaki KAWABE and Tsutomu WATANABE Synopsis: The study was
More informationViscosity of Ternary CaO-SiO2-Mx (F, O)y and CaO-Al2O3-Fe2O3 Melts Toshikazu YASUKOUCHI, Kunihiko NAKASHIMA and Katsumi MORI Synopsis : Effects of add
Viscosity of Ternary CaO-SiO2-Mx (F, O)y and CaO-Al2O3-Fe2O3 Melts Toshikazu YASUKOUCHI, Kunihiko NAKASHIMA and Katsumi MORI Synopsis : Effects of additives (Li2O, Na2O, K2O, MgO, BaO, Al2O3, Fe2O3, TiO2,
More information第 16 回 助 成 研 究 発 表 会 要 旨 集 ( 平 成 16 年 7 月 ) 発 表 番 号 23(31) 電 位 ノイズ 法 を 用 いた 製 塩 プラント 局 部 腐 食 モニタリング 技 術 への 極 値 統 計 解 析 手 法 の 適 用 に 関 する 基 礎 的 研 究 助 成 研 究 者 : 井 上 博 之 ( 大 阪 府 立 大 学 大 学 院 工 学 研 究 科 ) 近 年
More informationVol. 21, No. 2 (2014) W 3 mm SUS304 Ni 650 HV 810 HV Ni Ni Table1 Ni Ni μm SUS mm w 50 mm l 3 mm t 2.2 Fig. 1 XY Fig. 3 Sch
110 : 565-0871 2-1 567-0871 11-1 660-0811 1-9 - 1 tanigawa@jwri.osaka - u.ac.jp Influence of Laser Beam Profile on Cladding Layer TANIGAWA Daichi, ABE Nobuyuki, TSUKAMOTO Masahiro, HAYASHI Yoshihiko, YAMAZAKI
More information...Z...._.a..No.24-03J.indd
JFE J JFE No. 24 2009 8 p. 12 16 Waterproof Material JFE Eco-lami, and Waterproof System J-Eco proof MIYAKOSI Shohei OSIDA iroyuki IZUMI Mitsuhiko JFE JFE JFE JFE JFE J JFE -5 TPO Thermo plastic poly olefi
More information特-7.indd
Mechanical Properties and Weldability of Turbine Impeller Materials for High Temperature Exhaust Gas Turbocharger 1 000 1 050 246 IN100 The increase in environmental awareness in recent years has led to
More informationFundamental Study on the SOX Gas Sensor Utilizing Beta-Alumina with Sputtered Praseodymium Oxide Thin Films by Shinya YAO1*, Kenji MIYAGAWA1, Shigeru
Fundamental Study on the SOX Gas Sensor Utilizing Beta-Alumina with Sputtered Praseodymium Oxide Thin Films by Shinya YAO1*, Kenji MIYAGAWA1, Shigeru IIJIMA2 and Zensaku KOZUKA1 1. Faculty of Engineering,
More information特-4.indd
1 000 Ni-Cr Tribological Characteristics of Ni-Cr Alloy at 1 000 C in Air R&D 1 000 Ni-Cr 1 000 Ni-Cr alloy sliding tests in atmosphere at 1 000 C were carried out and the process in which a glazed oxide
More information'76 S '24' :559.56: (278) オ ー ス テ ナ イ ト ス テ ン レ ス 鋼 の 高 温 高 圧 下 に お け る 応 力 水 素 割 れ に つ い て 早 稲 田大 学 理工 学 部 長 谷 川 正 義 野村 茂 雄 原
'76 S654 669.15'24'26-194.56:559.56:669.788 (278) オ ー ス テ ナ イ ト ス テ ン レ ス 鋼 の 高 温 高 圧 下 に お け る 応 力 水 素 割 れ に つ い て 早 稲 田大 学 理工 学 部 長 谷 川 正 義 野村 茂 雄 原敏夫 1.緒 名取 敦 言 著 者 ら は これ ま で オ ー ス テ ナ イ ト ス テ ン レ
More informationブック 1.indb
Zn めっき 鋼 板 ならびに 溶 融 6%Al-3%Mg 合 金 めっき 鋼 板 の 防 食 機 構 9 レビュー Zn めっき 鋼 板 ならびに 溶 融 6%Al-3%Mg 合 金 めっき 鋼 板 の 防 食 機 構 浦 中 将 明 * 清 水 剛 ** Corrosion Resistance Mechanism of Zn Coated Steel Sheet and Hot-dip 6%Al-3%Mg
More information16 Dissolution Rate of Alumina into Molten CaO-SiO2--Al2O3-MgO Slags Shoichirou TAIRA, Kunihiko NAKASHIMA and Katsumi MORI Synopsis : Dissolution rate
16 Dissolution Rate of Alumina into Molten CaO-SiO2--Al2O3-MgO Slags Shoichirou TAIRA, Kunihiko NAKASHIMA and Katsumi MORI Synopsis : Dissolution rates of sintered alumina into molten CaO-SiO2-9mass%Al2O3-10mass%MgO
More informationDJ618_06_火力発電所_05[029-033].indd
技 術 紹 介 火 力 発 電 ボイラにおける 高 温 硫 化 腐 食 茂 田 潤 一 * S h i g e t a J u n - i c h i 石 炭 焚 きボイラの 火 炉 水 壁 管 等 の 熱 放 射 領 域 では 燃 焼 ガス 雰 囲 気 中 に 発 生 する 硫 化 水 素 (H2S) 石 炭 中 に 存 在 するパイライト(FeS2) NOx 低 減 のための 還 元 燃 焼 等
More informationInfluence of Material and Thickness of the Specimen to Stress Separation of an Infrared Stress Image Kenji MACHIDA The thickness dependency of the temperature image obtained by an infrared thermography
More informationThe Effect of the Circumferential Temperature Change on the Change in the Strain Energy of Carbon Steel during the Rotatory Bending Fatigue Test by Ch
The Effect of the Circumferential Temperature Change on the Change in the Strain Energy of Carbon Steel during the Rotatory Bending Fatigue Test by Chikara MINAMISAWA, Nozomu AOKI (Department of Mechanical
More informationNippon Suisan Gakkaishi 55 (10), (1989) ) Effects of ph and Sodium Chloride on the Water Holding Capacity of Surimi and its Gel Yoshiaki Aka
Nippon Suisan Gakkaishi 55 (10), 1827-1832 (1989) ) Effects of ph and Sodium Chloride on the Water Holding Capacity of Surimi and its Gel Yoshiaki Akahane*2, and Yutaka Shimizu*3 Water in Alaska pollack
More informationB_01田中.indd
A Study on the Image of the City in Contemporary Korea: Democracy and Busan Satoru Tanaka Abstract Busan has been the biggest harbor city in Korea, and ranked as one of the centers in democratization history
More informationFig. 1. Relation between fatigue crack propagation rate and stress intensity factor range. Fig. 2. Effect of stress ratio on fatigue crack opening rat
Fatigue Crack Propagation and Fracture Surface in Polyvinyl Chloride by Tetsuro SHIRAISHI The fatigue crack propagation behavior and the fracture surface appearance under several load conditions in polyvinyl
More informationTable 1 Properties of parent coals used Ebenezer, Massel Buluck ; Australia, Datong; China Table 2 Properties of Various chars CY char: Captured char
Table 1 Properties of parent coals used Ebenezer, Massel Buluck ; Australia, Datong; China Table 2 Properties of Various chars CY char: Captured char by cyclone char: Carbonized char at 1273 K 気流 層 石 炭
More information渡辺(2309)_渡辺(2309)
[ 29 p. 241-247 (2011)] ** *** ** ** Development of a nickel-based filler metal containing a small amount of silicon by WATANABE Takehiko, WAKATSUKI Ken, YANAGISAWA Atsusi and SASAKI Tomohiro Authors tried
More informationMikio Yamamoto: Dynamical Measurement of the E-effect in Iron-Cobalt Alloys. The AE-effect (change in Young's modulus of elasticity with magnetization
Mikio Yamamoto: Dynamical Measurement of the E-effect in Iron-Cobalt Alloys. The AE-effect (change in Young's modulus of elasticity with magnetization) in the annealed state of iron-cobalt alloys has been
More information378-07版下
Zinc Alloy Coated Steel Wire with High Corrosion Resistance Abstract To improve the corrosion resistance of Zn coating and Zn-Al alloy coating for steel wires, Zn-Al-Mg alloy has been developed. In this
More information*.....J.....S.q..2013B_....
1 1 2 2 3 3 4 4 5 6 5 7 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60 61 62 63 64 65 66
More informationThe Evaluation of LBB Behavior and Crack Opening Displacement on Statically Indeterminate Piping System Subjected to Monotonic Load The plastic collap
The Evaluation of LBB Behavior and Crack Opening Displacement on Statically Indeterminate Piping System Subjected to Monotonic Load The plastic collapse and LBB behavior of statically indeterminate piping
More information2
1 2 3 4 ス イ ッ チ 5 6 7 6.6m 2 123-4567-8910 123-4567- 8 123-4567-8910 123-4567- 9 () 10 () 11 12 () 13 14 ) 15 16 17 18 ++ 19 20 21 22 23 の 24 25 26 27 28 ( ) ( ) 29 ( ) ( ) 30 31 32 33 34 35 36 37 6.6m
More information年次大会原稿最終.PDF
Structural Analysis of Coating Layer Containing Plastic Pigments Yoko Saito, Hideki Touda, Junji Kasai ZEON Corporation Hitomi Hamada, Toshiharu Enomae, Fumihiko Onabe The University of Tokyo Recently,
More information「消える」金融、「創る」金融-2010年のリテール金融
2010 2010 CONTENTS 1 2 3 4 18 20066 1 2 19 20 20066 3 1 12 21 2 22 20066 3 4 23 1 1997 1997 1984 1893 1983 1980 2001 1990 1990 24 20066 1 260 26,418 213,597 239,416 1720062 25 2 3 26 20066 3 5 27 4 4 44
More information14 FEM [1] 1992 [3] 1(a)(b) 1(c) [2] 2 ( 財 ) 日本海事協会 36 平成 14 年度 ClassNK 研究発表会
1. 1(1) 1(2)[1] 1992 [2] 1992 [3] 100 100 比率 (%) 80 60 40 変形腐食亀裂 相対損傷数 80 60 40 変形腐食亀裂 20 20 0 0 5 10 15 20 25 船齢 ( 年 ) 0 0 5 10 15 20 25 船齢 ( 年 ) (1) Ratio of Each Damage (2) Number of Damage Fig.1 Relation
More informationCONTENTS 2012 2 Vol.65 No.2 ~~~~~~~~~~~~~~~~~~~~~~~~~~~~~~~ ~~~~~~~~~ ~~~~~~~~~~~~~~~~~~~~~~~~~~~~~~~ ~~~~~~~~~
2 2012 CONTENTS 2012 2 Vol.65 No.2 ~~~~~~~~~~~~~~~~~~~~~~~~~~~~~~~ ~~~~~~~~~ ~~~~~~~~~~~~~~~~~~~~~~~~~~~~~~~ ~~~~~~~~~ 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30
More informationCONTENTS 20103 Vol.63 No.3 ~~~~~~~~~~~~~~~~~~~~~~~~~~~~~~~ ~~~~~~~~ ~~~~~~~~
3 2010 CONTENTS 20103 Vol.63 No.3 ~~~~~~~~~~~~~~~~~~~~~~~~~~~~~~~ ~~~~~~~~ ~~~~~~~~ 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42
More information01.indd
2 Vol. 27 1 1 2 2 4 Vol. 27 Contents 3 Vol. 27 2 01 02 03 04 14 24 28 37 38 4 Vol. 27.01 5 Vol. 27.01 6 Vol. 27 7 Vol. 27.01 8 Vol. 27.02 9 Vol. 27.02 10 Vol. 27 11 Vol. 27.02 12 Vol. 27 13 Vol. 27.02
More informationEffect of Autofrettage on Fatigue Crack Growth Rate for High Pressure Reactors For high pressure reactor vessels such as for polyethylene production,
Effect of Autofrettage on Fatigue Crack Growth Rate for High Pressure Reactors For high pressure reactor vessels such as for polyethylene production, autof rettage is used extensively to have the fatigue
More informationA Study on the Influence of the Fluctuation of Source Voltage during Spot Welding on the Strength of Weld* By Tatsuya Hashimoto** Kinzi Tanuma** Abstr
A Study on the Influence of the Fluctuation of Source Voltage during Spot Welding on the Strength of Weld* By Tatsuya Hashimoto** Kinzi Tanuma** Abstract It is well known that even a-slight fluctuation
More information(1 ) (2 ) Table 1. Details of each bar group sheared simultaneously (major shearing unit). 208
2463 UDC 621.771.251.09 : 621.791.94: 669.012.5 Improvement in Cold Shear Yield of Bar Mill by Computer Control System Koji INAZAKI, Takashi WASEDA, Michiaki TAKAHASHI, and Toshihiro OKA Synopsis: The
More information第七回道路橋床版シンポジウム論文報告集 Experimental Study on Fatigue Resistance of RC Slab with UFC Panel for Wheel Running Fatique Test * ** ** *** **** Kazuhiko Minaku
第七回道路橋床版シンポジウム論文報告集 Experimental Study on Fatigue Resistance of RC Slab with UFC Panel for Wheel Running Fatique Test ************ Kazuhiko Minakuchi, Tadashi Abe, Tetsukazu Kida, Satoshi Tanaka and Yuuki
More information<5461726F2D303830333331817990568B8C2D8AAE915394C5817A819A202474>
食 品 添 加 物 等 の 規 格 基 準 の 一 部 を 改 正 する 件 新 旧 対 照 条 文 食 品 添 加 物 等 の 規 格 基 準 ( 昭 和 34 年 厚 生 省 告 示 第 370 号 ) 平 成 0 年 3 月 31 日 改 正 改 正 後 改 正 前 ( 傍 線 部 分 は 改 正 部 分 ) 第 4 おもちや 第 4 おもちや A おもちや 又 はその 原 材 料 の 規 格
More information388599-P036-P041
Die life improvement of flat type punches for hot forging Morihiko Nakasaki, Koji Era, Hiroyuki Myochin and Ichiro Takasu Synopsis: Since forged products have been required more complex and net-shape,
More information<4D F736F F D E939A88C F087542D315F3289F196DA E69>
H24 選択科目 Ⅰ-1 答案解答鉄筋コンクリート構造物の工事に関して 以下の問いに答えよ 1. 鉄筋コンクリートの品質管理について 3つ挙げて説明せよ (1.5 枚程度 ) 2. 鉄筋腐食の主な原因と対処法について述べよ また 鉄筋 1 腐食の補修方法について3つ挙げて説明せよ (1.5 枚程度 ) 記入者 作成日 2012.8.19 科目 選択科目 履歴 2 問題番号 選択科目 建設 科目 選択科目施工計画及び施工
More informationTitle インジウムを添加した Ag-Au-Cu-Pd 系合金の物性 Author(s) 時崎, 照彦 ; 服部, 雅之 ; 小田, 豊 Journal 歯科材料 器械, 26(5-6): URL Right Post
Title インジウムを添加した Ag-Au-Cu-Pd 系合金の物性 Author(s) 時崎, 照彦 ; 服部, 雅之 ; 小田, 豊 Journal 歯科材料 器械, 26(5-6): 367-374 URL http://hdl.handle.net/10130/420 Right Posted at the Institutional Resources for Unique Colle
More information高濃度硫化水素削減のための汚泥脱気装置の開発
5-(1)-2 高 濃 度 硫 化 水 素 削 減 のための 汚 泥 脱 気 装 置 の 開 発 計 画 調 整 部 技 術 開 発 課 廣 繁 直 治 山 下 博 史 ( 現 経 理 部 業 務 管 理 課 ) 1. 目 的 東 京 都 区 部 で は 汚 泥 処 理 の 効 率 化 を 図 る た め に 集 約 処 理 を 進 め て い る 汚 泥 の 集 約 処 理 の 進 展 と と も
More informationMicrosoft Word - ②270717【お知らせ】原因調査報告について(局HP用)
平 成 27 年 7 月 17 日 中 国 四 国 防 衛 局 お 知 らせ 岩 国 飛 行 場 内 で 発 生 した 航 空 機 用 燃 料 の 油 漏 れ 事 案 に 関 する 原 因 調 査 の 報 告 について 平 成 27 年 1 月 20 日 岩 国 飛 行 場 内 において 燃 料 配 管 工 事 に 関 して 配 管 に 燃 料 を 通 す 試 験 中 に 発 生 した 漏 油 事
More information24 Depth scaling of binocular stereopsis by observer s own movements
24 Depth scaling of binocular stereopsis by observer s own movements 1130313 2013 3 1 3D 3D 3D 2 2 i Abstract Depth scaling of binocular stereopsis by observer s own movements It will become more usual
More informationMicrosoft Word - 20年度のまとめ090316.doc
ねじの 腐 食 寿 命 予 測 と 試 験 方 法 の 検 討 (Ⅲ) 関 西 ねじ 協 同 組 合 研 究 開 発 委 員 会 表 面 処 理 グループ 1.はじめに 建 築 構 造 物 の 屋 根 や 外 壁 などを 締 結 するねじなどのファスナー 金 物 は 近 年 安 全 や 環 境 対 策 およびコスト 低 減 のために 素 材 や 表 面 処 理 製 品 を 問 わず 多 くの 部 材
More information1006最 近 熔 鉄 が凝 固す れ ばMgの は析 出す る.そ 沸 点 は1100 ).こ 鐵 材 料 で はMgは の 析 出 したMg 蒸気 が そ の 時 析 出 す る黒 鉛 片 に 吸 着 され て,そ 性 を 著 し く増 す.著 鑄 溶解 度が減 るか ら大 部 分 のMg の 時 の温 度1150 1200 蒸 気 で あ る(Mgの の の変 形 し く変 形 し易 くなつ
More information52-2.indb
Jpn. J. Health Phys., 52 (2) 55 60 (2017) DOI: 10.5453/jhps.52.55 * 1 * 2 * 2 * 3 * 3 2016 10 28 2017 3 8 Enhancement of Knowledge on Radiation Risk Yukihiko KASAI,* 1 Hiromi KUDO,* 2 Masahiro HOSODA,*
More information塗装深み感の要因解析
17 Analysis of Factors for Paint Depth Feeling Takashi Wada, Mikiko Kawasumi, Taka-aki Suzuki ( ) ( ) ( ) The appearance and quality of objects are controlled by paint coatings on the surfaces of the objects.
More informationInstability of Aerostatic Journal Bearings with Porous Floating Bush at High Speeds Masaaki MIYATAKE *4, Shigeka YOSHIMOTO, Tomoaki CHIBA and Akira CH
Instability of Aerostatic Journal Bearings with Porous Floating Bush at High Speeds Masaaki MIYATAKE *4, Shigeka YOSHIMOTO, Tomoaki CHIBA and Akira CHIBA Department of Mechanical Engineering, Tokyo University
More informationDevelopment of Induction and Exhaust Systems for Third-Era Honda Formula One Engines Induction and exhaust systems determine the amount of air intake
Development of Induction and Exhaust Systems for Third-Era Honda Formula One Engines Induction and exhaust systems determine the amount of air intake supplied to the engine, and as such are critical elements
More informationTable 1 Type of polymeric coating materials Fig. 2 Results of suppressive effects of polymeric coating materials on the progress of neutralization of concrete. Table 2 Evaluation of the suppressive effects
More information106(18) 原 使 用 した 測 定 部 位 は 期 門 穴相 当部 位 の 表 皮 上 及 び 真 皮 下 と し, 表 皮上 で は 艾 柱 の 直 下 に 熱 電 対 先 端 を露 出 し固 定 した 真 皮 下 で は施 灸部 より10mm 下 方 を切 開 剥 離 し, 施 灸 部 直
106(18) 原 使 用 した 測 定 部 位 は 期 門 穴相 当部 位 の 表 皮 上 及 び 真 皮 下 と し, 表 皮上 で は 艾 柱 の 直 下 に 熱 電 対 先 端 を露 出 し固 定 した 真 皮 下 で は施 灸部 より10mm 下 方 を切 開 剥 離 し, 施 灸 部 直 下 に 熱 電 対 先端 が 届 くよ うに挿 入 した 熱 電 対 の 出 力 は 温 度 モ ジュ
More information浸炭焼入れ鋼の化学研磨処理
27 Chemical Polishing Process of Carburized Steel Ken-ichi Suzuki, Masaki Kajino, Fumio Shimizu HF-H 2 O 2 H 2 O 2 H 2 O 2 HF Carburized steel, which is widely used for transmission gears, has an abnormal
More informationJ. Soc. Cosmet. Chem. Jpn. 7-chome, Edogawa-ku, Tokyo 132, Japan 2.1 J. Soc. Cosmet. Chem. Japan. Vol. 31, No
J. Soc. Cosmet. Chem. Jpn. 7-chome, Edogawa-ku, Tokyo 132, Japan 2.1 J. Soc. Cosmet. Chem. Japan. Vol. 31, No. 2 1997 167 Fig.-1 Balanced fiber method Fig.-2 The effects of perming and IG on breaking off
More informationX線分析の進歩45
Advances in X-Ray Chemical Analysis, Japan, 45 (2014) ISSN 0911-7806 NaCl Color Center in NaCl Takuya TSUJI, Hiroyuki IWASAKI and Jun KAWAI NaCl Color Center in NaCl Takuya TSUJI, Hiroyuki IWASAKI and
More informationFig. 1. Block diagram of the apparatus for analysis of carbon in steel. (a) Steel sample (cleaned) (b) Steel sample (contaminated) (c) Air was intenti
Determination of Ultra-low Content of Carbon in Steel by Infrared Absorptiometry after Combustion in Electro Resistance Furnace Yukihiro KURAKAKE, Tomoyuki ICHIOKA, Kiyoyuki TANAKA and Morihiro HASEGAWA
More information電子部品はんだ接合部の熱疲労寿命解析
43 Evaluation for Thermal Fatigue Life of Solder Joints in Electronic Components Haruhiko Yamada, Kazuyoshi Ogawa 2 63Sn- 37Pb 95Pb-5Sn Si Cu Si 63Sn-37Pb Since automotive electronic components are used
More information<4D F736F F D F4390B35F96688E4B8BA689EF817A976E975A889F899482DF82C182AB93538BD882C E838A815B836782CC AB945C2E646F63>
溶 融 亜 鉛 めっき 鉄 筋 とコンクリートの 付 着 性 能 について デンロコーポレーション 今 野 貴 史 那 須 電 機 鉄 工 盛 永 康 文 森 純 一 郎 横 浜 ガルバー 渡 会 竹 志 田 中 剣 治 シーケー 金 属 大 橋 一 善 西 田 雄 治 ガルバ 興 業 菊 川 美 仁 1.はじめに 我 が 国 の 社 会 資 本 は 今 一 斉 に 更 新 時 期 を 迎 えているが
More information資源と素材
(Shigen to Sozai) Vol.116 p. 285 290 (2000) 共存硫酸塩を含む強酸性 MnSO 4 溶液中のオゾン酸化によって生成した沈殿の X 線回折および放電特性 * 西村忠久 1 梅津良昭 2 X-ray Diffraction and Discharge Behavior of Precipitates Produced by Ozone Oxidation in
More information磁気測定によるオーステンパ ダクタイル鋳鉄の残留オーステナイト定量
33 Non-destructive Measurement of Retained Austenite Content in Austempered Ductile Iron Yoshio Kato, Sen-ichi Yamada, Takayuki Kato, Takeshi Uno Austempered Ductile Iron (ADI) 100kg/mm 2 10 ADI 10 X ADI
More information橡
Mein Grad. Eng Univ. Fri'kill, Vol. 61 March 20 I 3) Effects of Saline-Water Volume on Production Performance of Tubular Solar Still Hiroaki TERASAKI*, Takahiro YAMAJI" and Teruyuki FUKUHARA. (Received
More informationFig. 2 Effect of oxygen partial pressure on interfacial tensions between molten copper and fayalite slag (Fe/Si0 2=1.23) at 1473 K. Fig. s Effect or o
Fig. 1 Schematic diagram of the apparatus for measurements of interfacial tension by sessile drop method. Fig. 2 Effect of oxygen partial pressure on interfacial tensions between molten copper and fayalite
More information無電解めっきとレーザー照射による有機樹脂板上へのCuマイクロパターン形成
Title 無電解めっきとレーザー照射による有機樹脂板上への Cu マイクロパターン形成 Author(s) 菊地, 竜也 ; 和智, 悠太 ; 坂入, 正敏 ; 高橋, 英明 ; 飯野, 潔 ; 片山, 直樹 Citation 表面技術, 59(8): 555-561 Issue Date 2008-08 Doc URL http://hdl.handle.net/2115/36647 Type
More informationRate of Oxidation of Liquid Iron by Pure Oxygen Shiro BAN-YA and Jae-Dong SHIM Synopsis: The rate of oxidation of liquid iron by oxygen gas has been s
Rate of Oxidation of Liquid Iron by Pure Oxygen Shiro BAN-YA and Jae-Dong SHIM Synopsis: The rate of oxidation of liquid iron by oxygen gas has been studied using a volume constant technique. The process
More information錫-亜鉛-アルミニウム系鉛フリーはんだの実用化
- Practical Use of Lead-Free Tin-Zinc-Aluminum (Sn-Zn-Al) Solder - - - - - Abstract Fujitsu has implemented a company-wide effort to progressively reduce the use of lead and eventually eliminate this environmental
More informationSafety Performance of Steel Deck Plate (Flat Decks) Used for Concrete Slab Moulding CONTENTS 1. Introduction ---------------------------------------------------------------- (2) 2. Flat Decks ------------------------------------------------------------------
More information<836F83438393835F332E706466>
10 202 OCTOBER 研 究 開 発 現 場 から 06 挑 戦 てま 夢 もづくり 名 古 屋 製 鉄 所 錫 メッキ 工 場 冷 延 調 質 課 四 釜 忠 明 (2003 年 入 社 物 質 工 学 専 攻 ) 技 術 者 とて 確 か 足 跡 残 Series 自 動 車 や 家 電 製 品 ス チ ー ル 缶 ど 材 料 と る 冷 延 薄 板 製 品 は 用 途 応 じ て 連
More informationOn the Variation of Oxygen and Alminium in Molten Steel during Pouring Practice T. Obinata et, alii. Spoon position: (A): within 100mm under nozzle (B
On the Variation of Oxygen and Alminium in Molten Steel during Pouring Practice T. Obinata et, alii. Spoon position: (A): within 100mm under nozzle (B): 1000mm Fig. 1. Influence of the sampling methods
More informationJFE(和文)No.4-12_下版Gのコピー
JFE No. 4 245 p. 6358 Electrical Steels for Advanced Automobiles Core Materials for Motors, Generators, and High-frequency Reactors SENDA Kunihiro JFE NAMIKAWA JFEMisao HAYAKAWA JFEYasuyuki JNE JNEH JGE
More informationNobujiro Tsuchiya, Osamu Terada and Hisashi Suzuki : Some Properties of Titanium Carbide Layer Coated on WC-Co Alloy by CVD. The microstructure, hardn
Nobujiro Tsuchiya, Osamu Terada and Hisashi Suzuki : Some Properties Titanium Carbide Layer Coated on WC-Co Alloy by CVD. The microstructure, hardness and adhesive strength titanium carbide (TiC) layer
More informationContinuous Cooling Transformation Diagrams for Welding of Mn-Si Type 2H Steels. Harujiro Sekiguchi and Michio Inagaki Synopsis: The authors performed
Continuous Cooling Transformation Diagrams for Welding of Mn-Si Type 2H Steels. Harujiro Sekiguchi and Michio Inagaki Synopsis: The authors performed a series of researches on continuous cooling transformation
More informationPowerPoint プレゼンテーション
鉄 筋 腐 食 抑 制 タイプ RC 構 造 物 用 含 浸 系 表 面 保 護 材 取 扱 : 関 西 ペイント 株 式 会 社 国 内 総 代 理 店 :BASFジャパン 株 式 会 社 建 設 化 学 品 事 業 部 プロテクトシルCITの 効 果 鉄 筋 コンクリート 構 造 物 全 般 の 長 寿 命 化 対 策 として 有 効 コンクリート 表 面 に 塗 布 するだけで 鉄 筋 の 腐
More informationTable 1. Shape and smelting properties of chrome ores as delivered. Table 2. Chemical composition of chrome ores (%). Table 3. Chemical composition of
UDC 669.263.1: 669.046.462 The Reduction Process and Reducibility of Chromite with Carbon Hiroshi G. KATAYAMA and Akihiko TANAKA Synopsis: In the present work, various chrome ores and relatively pure chromites
More informationuntitled
3 4 4 2.1 4 2.2 5 2.3 6 6 7 4.1 RC 7 4.2 RC 8 4.3 9 10 5.1 10 5.2 10 11 12 13-1 - Bond Behavior Between Corroded Rebar and Concrete Ema KATO* Mitsuyasu IWANAMI** Hiroshi YOKOTA*** Hajime ITO**** Fuminori
More information2. 損 傷 状 況 調 査 および 構 造 安 全 性 の 評 価 2.1 対 象 橋 梁 今 回 の 調 査 検 討 で 対 象 とした 神 取 橋 は 写 真 -1 および 図 -3に 示 す 1965 年 に 建 設 された3 径 間 連 続 下 路 式 トラス 橋 +3 連 単 純 合 成
神 取 橋 の 補 修 塗 装 に 関 する 調 査 検 討 * 若 山 昌 彦 ** 斎 藤 一 彦 *** 安 波 博 道 **** 中 島 和 俊 1.はじめに 1 1.1 目 的 と 概 要 トラス 格 点 部 や 桁 端 部 などの 局 所 に 腐 食 損 傷 が 生 じた 神 取 橋 について 鋼 橋 の 長 寿 命 化 を 志 向 し た 局 部 補 修 塗 装 工 法 の 適 用 を
More information国土技術政策総合研究所 研究資料
ISSN TECHNICAL NOTE of National Institute for Land and Infrastructure Management No256 September 2005 Experimental Study on Seismic Behavior of Seawalls for Controlled Waste Disposal Shingo KANO, Katsuya
More informationŁI’ÜTmŸ_Ł¶color
191997 217 227 Journal of the Geotherrmal Research Society of Japan Vol.19,No4.(1997) P.217~P.227 Timing of Fracture Development Deduced from Microthermometry of Fluid Inclusions in Minerals from the Hijiori
More information